zilaee A, Farbod M. The effect of annealing temperature on electrical and optical properties of transparent and conductive thin films fabicated of multi-walled carbon nanotube/Ag nanowires. IJPR. 2017; 16 (4) :319-326
URL: http://ijpr.iut.ac.ir/article-1-2231-en.html

Department of physics, Shahid Chamran University, Ahvaz, Iran , zilaie_a@scu.ac.ir
Abstract:   (2397 Views)

Transparent and conductive thin films of multi-walled carbon nanotube/ Ag nanowires were fabricated using spin coating technique. In order to improve the electrical conductivity and the optical properties, the layers were annealed from room temperature to 350 °C for 30 minutes. The measurements revealed that annealing caused electrical conductivity of fabricated thin layes to be improved. The optimum annealing temperature for improving these properties was deduced 285 °C. For all different film thicknesses from about 89 to 183 nm it was observed that the presence of nanowires has improved the film’s electrical conductivity in all tempretures. The best ratio of DC conductivity to optical conductivity of the films, which is accounted as films figure of merit, was measured at 285 °C for all Ag percentages. Sheet resistance and optical transmittance were measured by four-point probe technique and UV-Vis spectrophotometer, respectively

Full-Text [PDF 14 kb]   (440 Downloads)    
Type of Study: Research | Subject: general

Add your comments about this article : Your username or email:
Write the security code in the box

Send email to the article author


© 2015 All Rights Reserved | Iranian Journal of Physics Research

Designed & Developed by : Yektaweb