انجمن فیزیک ایران مجلۀ پژوهش فیزیک ایران 1682-6957 16 1 2019 11 26 Wettability modification of graphene oxide thin film through the photocatalytic reduction تغییر ترشوندگی لایه اکسید گرافین با استفاده از کاهش به روش فوتوکاتالیستی 19 25 1173 10.18869/acadpub.ijpr.16.1.19 FA رضا آرام گروه فیزیک، دانشکده علوم، دانشگاه زنجان، زنجان Journal Article 2019 11 26 In this paper, the effect of photocatalytic reduction on hydrophilicity of graphene oxide nanosheets is presented. The graphene oxide nanosheets were prepared by oxidation and exfoliation of natural graphite. The prepared samples were exposed to UV irradiation in presence of TiO2 nanoparticles. Raman spectroscopy and atomic force microscopy show that roughness of the surface is increased due to increasing irradiation. Also, the hydrophilicity of samples by measuring the contact angle of micro-liter droplets of deionized water, showed that by increasing exposure time up to 8 hours the contact angle of samples in crease from about 27 degrees to about 89 degrees. در این مقاله نتایج اثر کاهش فوتوکاتالیستی بر آب‌دوستی ورقه‌های اکسید گرفین ارائه می‌‌گردد. ورقه‌های اکسید گرافین از طریق اکسید کردن گرافیت طبیعی و ورقه ورقه کردن آن با شوک مکانیکی تهیه شده و سپس در حضور نانوذرات دی اکسید تیتانیوم تحت تابش اشعه فرابنفش قرار گرفتند. طیف‌سنجی رامان و میکروسکوپ نیروی اتمی نشان دادند که با افزایش تابش میزان زبری در سطح افزایش می­یابد. همچنین میزان آب‌دوستی نمونه‌ها با اندازه‌گیری زاویه تماسی قطرات میکرولیتری آب دیونیزه، نشان داد که با افزایش مدت زمان تابش تا 8 ساعت زاویه تماسی نمونه‌ها از حدود 27 درجه تا حدود 89 درجه افزایش می­یابد. https://ijpr.iut.ac.ir/article_1173_0a0a0c8aaa00ade50f74a3f0ca981ed7.pdf