انجمن فیزیک ایران مجلۀ پژوهش فیزیک ایران 1682-6957 9 1 2019 11 26 The effect of Ni and Fe doping on YBCO powder prepared by sol gel method اثر آلایش Ni و Fe در ترکیب ابررسانای YBCO ساخته شده به روش سل ـ ژل 29 33 788 FA فاطمه صائب سمیه فلاحتی وحید دادمهر Journal Article 2019 11 26  We fabricated YBa2Cu3-xMxO7- d (M=Ni, Fe) bulk samples, with stochiometric amount 0≤x≤0.045 by sol-gel method. The phase analysis and microstructure of specimens were examined by XRD and SEM. The electrical resistivity was measured using standard four probe technique for 77-300K. Investigation of XRD spectrum by MAUD shows Ni and Fe ions substitute in Cu(2) and Cu(1) site, respectively. Transition temperature decreases in 93-87K for Ni-doped samples and 93-92K for Fe-doped series. It seems that the suppression of superconductivity has no direct correlation with the magnetism of ions itself .   نمونه‌های بس­بلوری M=Ni,Fe) YBa2cu3-xMxO7-δ  )با مقادیر آلایش 0≤x≤0/045 به روش سل-ژل ساخته شد. آنالیز فازی و ریز ساختار نمونه‌ها با طیف اشعه X و SEM مورد بررسی قرار گرفت . مقاومت الکتریکی با استفاده از تکنیک چهارمیله­ای استاندارد برای 300-77k  اندازه‌گیری شده‌اند. نتایج بررسی طیف XRD ، با استفاده از نرم افزار MAUD جانشینی Ni در محل (2) Cu و Fe در محل (1) Cu را نشان می‌دهد. تغییرات دمای گذار برای نمونه­های آلاییده با Ni در گستره 93-87k و برای آلایش Fe در محدوده 93-92k بوده است. به نظر می‌رسد کاهش دمای گذار در این ترکیبات ارتباط مستقیمی با مغناطیس آلاینده­ها ندارد. https://ijpr.iut.ac.ir/article_788_c15da1f2b5e5ed6e6837a3802f0d1593.pdf