Iranian Journal of Physics Research

Synthesis of hydroxyapatite nanoparticles by the Sol-Gel method, investigation of its morphology and comparison of its structure with intact tooth

Document Type : Original Article

Authors

S Mohammadi Aref 1
M Safarigezaz 1
M Khatamian 2

1 Department of Physics, Faculty of Physics, Tabriz University, Tabriz, Iran

2 Department of Chemistry, Faculty of Chemistry, Tabriz University, Tabriz, Iran

https://doi.org/10.47176/ijpr.20.3.31022
Abstract
In this study, calcium nitrate tetrahydrate (Ca (NO3)2.4H2O) and phosphorus pentoxide (p < sub>2O5) were used to synthetize hydroxyapatite nanoparticles through the sol-gel method at the ambient temperature. In order to examine the structure and identify the chemical bonds and to compare them with the  intact tooth, X-ray diffraction analysis (XRD) and Fourier transform infrared spectrum (FT-IR) were used, respectively. Also, through scanning electron microscope (SEM) images, the microstructure and morphology of both synthesized hydroxyapatite nanoparticles and intact tooth were investigated. The results of X-ray diffraction analysis and Fourier transform infrared spectrum indicated  that the produced powder was  pure hydroxyapatite, i.e. without any discernible amount of impurity in the sample. Crystal structure of the synthesized hydroxyapatite was  nearly identical to the crystal structure of intact tooth; moreover,  the chemical bonds of the  intact tooth were also seen in hydroxyapatite. Furthermore, the synthesized sample featured a high degree of crystallinity. On the other hand, analysis of SEM images showed  that the morphology of the synthesized hydroxyapatite and intact tooth (with nanoscale dimensions and average particle size distribution of 25.69 nm and 23.15 nm, respectively), was almost spherical, thereby confirming the similarity of  the synthesized nanoparticle structure to thr intact tooth. In these images, the agglomeration of the synthesized nanoparticles was also seen. Compressive strength of the synthesized sample was equal to  5.5 MPa, which was approximately the same as that  of the  cancellous bone.

Keywords

hydroxyapatite
tooth
sol-gel
nanoparticle
microstructure
  1. B H Fellah, N Josselin, D Chappard, P Weiss, and P Layrolle, J. Mater. Sci. Mater. Med. 18 (2007) 287.

  2. M. safari Gezaz, S. Mohammadi Aref, and M. Khatamian, Mater. Chem. Phys. 226 (2019) 169.

  3.  H Badran, I S Yahia, M S Hamdy, and N S Awwad, Radiat. Phys. Chem. 130 (2017) 85.

  4. Kh R Mohamed, H H Beherei, G T El Bassyouni, and N El Mahallawy, Mater. Sci. Eng. C. 33 (2013) 4126.

  5. A Biancoa, I Cacciottia, M Lombardib, L Montanarob, E Bemporadc, and M Sebastianic, Ceram. Int. 36 (2010) 313.

  6. T Guo, W Kang, D Xiao, R Duan, W Zhi, and J Weng, Molecules. 19 (2014) 149.

  7. 7.   M R Saeri, A Afshar, M Ghorbani, N Ehsani, and C C Sorrell, Mater. Lett. 57 (2003) 4064.

  8. Y. Sun, G. Guo, D. Tao, and Z. Wang, J. Phys. Chem. Solids. 68 (2007) 373.

  9. M Toriyama, A Ravaglioli, A Krajewski, G Celotti, and A Piancastelli, J. Eur. Ceram. Soc. 16 (1996) 429.


10. C C Silva, A G Pinheiro, R S Deoliveira, J C Goes, N Aranha, L R Deoliveira. and A S B Sombra, Mater. Sci. Eng. C. 24 (2004). 


11. L Yuncao, C Bozhang, and J F Hung, Ceram. Int. 31 (2005) 1041.


12. I S Kim and P N Kumta, Mater. Sci. Eng. B. 111 (2004) 232.


13. D M Liu, Q Yang, T Troczynski, and W J Tseng, Biomaterials 23 (2002) 1679.


14. S Salehi and M H. Fathi, Ceram. Int. 36 (2010) 1659.


15. M Mazaheri, M Haghighatzadeh, A M Zahedi, and S K  Sadrnezhaad, J. Alloy. Comp. 471 (2009) 180.


16. M Eilbagi, R Emadi, K Raeissi, M Kharaziha, and A Valiani, Mater. Sci. Eng. C. 68 (2016) 603.


17. M Akao, H Aoki, and K Kato, J. Mater. Sci. 16 (1981) 809.


18. E Landi, A Tampieri, G Celotti, and S Sprio, J. Eur. Ceram. Soc. 20 (2000) 2377.


19. L Pierre, A Ito, and T Tateishi, J. Am. Ceram. Soc. 81 (1998) 1421.


22. M H Fathi and A Hanifi, Mater. Lett. 61 (2007) 3978.

Home

Guide for Authors

Submit Manuscript

Reviewers

Contact Us

تحت نظارت وف ایرانی