Abbasian H, Almasi Kashi M, Ramezani A, Khayatian A. The effect of different oxide layers on the sensing properties of anodic alumina nanoporous film. IJPR. 2014; 13 (4) :341-346
URL: http://ijpr.iut.ac.ir/article-1-816-en.html

, Abbasianhamed@gmail.com
Abstract:   (3929 Views)
In the present work, anodized aluminum oxide template was prepared by accelerated mild anodization technique in 0.6M phosphoric aside and 175 V, anodization voltage. Pore widening was performed by chemical etching in 0.5M phosphoric acid for 8, 16, 32, 40 minutes. Scanning Electron Microscopy (SEM) images showed the pores, diameter exponentially increases with etching time. By depositing silver contacts on the prepared samples and using an RC circuit for applying impedance spectroscopy, the characteristics of the humidity sensor based on constructed samples were investigated. The maximum response was seen for the sample etched for 40 minutes. For this sample, the detectable threshold of relative moisture was 30% and the response and the recovery time were 8, 2 seconds, respectively
Full-Text [PDF 275 kb]   (1093 Downloads)    
Type of Study: Research | Subject: General

Add your comments about this article : Your username or Email:
Write the security code in the box

Send email to the article author

© 2015 All Rights Reserved | Iranian Journal of Physics Research

Designed & Developed by : Yektaweb

تحت نظارت وف بومی آسپا-وف