In this research, Schottky diode with Al-PANI/MWCNT-Au structure was fabricated using spin coating of composite polymer and physical vapor deposition of metals. For this purpose, a thin layer of gold was coated on glass and then composite of polyaniline/multi-walled carbon nanotube was synthesized and spin-coated on gold layer. Finally, a thin layer of aluminum was coated on polymer layer. The current-voltage characteristics of diode were studied and found that I-V curve is nonlinear and nonsymmetrical, showing rectifying behavior. I-V characteristics plotted on a logarithmic scale for Schottky diode showed two distinct power law regions. At lower voltages, the mechanism follows Ohm’s Law and at higher voltages, the mechanism is consistent with space charge limited conduction (SCLC) emission. The parameters extracted from I-V characteristics were also calculated.
Keywords
2. S Jussila, M Puustinen, T Hassinen, J Olkkonen, H G O Sandberg, and K Solehmainen, Organic Electronics 13 (2012) 1308.
3. T Sekitani, H Nakajima, H Maeda, T Fukushima, T Aida, K Hata, and T Someya, Nat. Mater. 8 (2009) 494.
4. S F Tedde, J Kern, T Sterzl, J Frst, P Lugli, and O Hayden, Nano Lett. 9 (2009) 980.
5. R Bechara, J Petersen, V Gernigon, P Lévêque, T Heiser, V Toniazzo, D Ruch, and M Michel, Solar Energy Materials and Solar Cells 98 (2012) 482.
6. Y Chen, Z Jiang, M Gao, S E Watkins, P Lu, H Wang, and X Chen, Appl. Phys. Lett. 100 (2012) 203304.
7. K S Kang, Y Chen, H K Lim, K Y Cho, K J Han, J Kim, Thin Solid Films 517 (2009) 6096.
8. C Hyun Kim, O Yaghmazadeh, D Tondelier, Y B Jeong, Y Bonnassieux, and G Horowitz, J. Appl. Phys. 109 (2011) 083710.
9. V Saxena, and K S V Santhanam, Cur. Appl. Phys. 3 (2003) 227.
10. R K Gupta, and R A Singh, Mater. Sci. in Semicond. Proc. 7 (2004) 83.
11. A Hassanien, M Gao, M Tokumoto, and L Dai, Chem. Phys. Lett. 342 (2001) 479.
12. M Cochet, W K Maser, A M Benito, M A Callejas, M T Martinez, J M Benoit, J Schreiber, and O Chauvet, Chem. Commun. 1 (2001) 1450.
13. S A Curran, P M Ajayan, W J Blau, D L Carroll, J N Coleman, A B Dalton, A P Davey, A Drury, B McCarthy, S Maier, and A Strevens, Adv. Mater. 10 (1998) 1091.
14. P C Ramamurthy, W R Harrell, R V Gregory, B Sadanadan, and A M Rao, Synth. Metals 137 (2003) 1497.
15. S Bandyopadhyay, A Bhattacharyya, and S K Sen, J. Appl. Phys. 85 (1999) 3671.
16. S M Sze and K K Ng, “Physics of Semiconductor Devices”, 3rd ed., Wiley, New York (2007).
17. H Tomozawa, F Braun, S Phillps, A J Heeger, and H Kroemer, Synth. Metals 22 (1987) 63.
18. E H Rhoderick, R H Williams, “Metal Semiconductor Contacts”, second ed., Clarendon, Oxford, (1988).
19. K C Kao, W Hwang, “Electrical Transport in Solids”, Pergamon Press, Oxford (1981).
20. M A Lampert, P Mark, “Current injection in solids”, New York: Academic, (1970)
)