Thermoluminescence material LiF:Mg,Cu,P was produced using standard GR200 dopant concentrations and its emission and absorption spectrums was measured after beta irradiation. The alterations resulting from various thermal treatments, excessing the recommended temperatures namely 240ºC on the emission and absorption spectrums has been investigated. The main peak of absorption spectrum, which is relevant to F centers, don’t exhibits any difference to the absorption spectrum of LiF:Mg,Ti, which in turn demonstrates the dominant function of F centers in formation of trap centers in both TL materials. The TL Material LiF:Mg,Cu,P is sensitive to the temperatures higher than 240ºC and the results show that main peak of absorption spectrum shifts to lower wavelength with increasing the temperature to 400ºC. Furthermore the investigation of TL sensitivity from LiF:P at temperatures above 240ºC confirms the role of P impurity in sensitivity reduction from LiF:Mg,Cu,P at temperatures higher than 240ºC.
Keywords
2. Meijvogel, K., and Bos, A. J. J., Influence of Thermal Treatments on Glow Curve and Thermoluminescence Spectra of LiF(Mg,Cu,P), Rad. Meas. 24(3), 239-247 (1995)
3. Cai, G., Wu, F. and Zuo, J. Radiation Induced Damage and its Recovery to Thermoluminescence sensitivity of LiF:Mg,Cu,P Crystal. Radiat. Effects Defects Solid 132, 257-264 (1994)
4. Kaiyong T., Honying Z., and Wenxiu S., Thermal loss and Recovery of Thermoluminescence sensitivity in LiF:Mg, Cu,P, Rad. Prot. Dos. Vol. 90, pp. 449-452 (2000)
5. McKEEVER S.W.S., Measurments of emission spektra during thermoluminescence, (TL) from LiF (Mg, Cu, P) TL dosimeters, J. Phys. D: Appl. Phys. 24, . 988-996, (1991)
6. McKEEVER S.W.S., M. Moskovitch and P.D. Townsend, Thermoluminescence Dosimetry Materials, Properties and uses, Nuclear Technology Publishing, Ashford, Kent, U.K. ISBN 1-870965-19-1. Handbook, Chapter 3.1.1.1.c
7. T. C. Chen and T. G. Stoebe, Role of Copper in LiF:Mg,Cu,P Thermoluminescent Phosphors, Rad. Prot. Dos. Vol. 2, No. 2, pp. 101-106 (1998)
8. Jain V. K. Kathuria S. P. and Gangary A. K. Radiation damage in Thermoluminescent LiF:TLD phosphor, J. Phys C., 8, 2191, 1975
)