Iranian Journal of Physics Research

Study the effect of ion type on the transport properties of implanted tantalum interfaces of multilayer structures

Document Type : Original Article

Authors

Amir hoshang Ramezani
Somayeh Asgary
Zhaleh Ebrahiminezhad

Department of Physics, West Tehran branch Azad Unuversity, Tehran , Iran

https://doi.org/10.47176/ijpr.23.2.11407
Abstract
In this paper, the effect of ion type has been considered to study transport through the structures in which their interfaces have been produced by the ion implantation process. The interfaces are tantalum based and the argon and nitrogen ions have been considered at an energy of 30 keV and in different doses at ambient temperatures. For studying the surface morphology of the ion implanted rough thin films, The Atomic Force Microscopy (AFM) analysis has been used. The average roughness has been determined. Decreasing the transmission probability is the main outcome of the rough interfaces/samples. The results show that the interfaces which have been produced by argon ion implantation are rougher than nitrogen cases. Also, the peak to valley ratio reduces in two cases. Moreover, with increasing nitrogen ion doses, the current density has been reduced as a function of voltage. As it is predicted, the transmission probability decreases because of the rough interfaces which have been generated by ion implantation process. As a consequence of the scattering process (because of the interfacial roughness), the resonant tunneling peak current decreases and also, the peak to valley ratio (PVR) reduces. The samples which were prepared by argon ion implantation were rougher than nitrogen ones. Also, with increasing the nitrogen ion doses, the current density has been decreased as a function of voltage.

Keywords

tantalum thin film
roughness
Subjects
  1. S S Patila, et al., Surface & Coatings Technology 196  ( 2005) 284.
  2. P Budzynskia et al., Vacuum 78 ( 2005) 658.
  3. C M Fang, et al., Journal of Materials Chemistry  11 (2001) 1248.
  4. Zh-H Cui and H  Jiang,  Phys. Chem. C  121 ( 2017) 3241.
  5. K Panda, Journal of Applied Physics 110 (2011) 044304.
  6. Y Z Liu, et al., Nucl .Instr. Meth.Phys .Res.B 237 (3-4) (2005) 543.
  7. S S Patila, etal., Surface & Coatings Technology 196 (2005) 
  8. P Budzynskia, et al., Vacuum 78 (2005) 685.
  9. A K De, et al., Trans. A 37 (2006) 1875.
  10. Z W Kowalski, et al., Vacuum 83 (2009)
  11. R Skomski, Journal of Physics Condensed Matter 15 ( 2003) R841.
  12. C L Dennis, et al., Journal of Physics Condensed Matter 14 (2002) R1175.
  13. A Czir ́aki, et al., Thin Solid Films 433 (2003) 237.
  14. Y Shiota, et al., Nature Materials 11 (2012) 39.
  15. P Zahn and I Mertig, Materials Physics 63 (2001) 104412.
  16. P X  Xu, Physical Review B 73 (2006) 180402R.
  17. Y Li and Ch.-Ray Chang, Physics Letters A 287  (2001) 415.
  18. A Koley, et al., Applied Sciences 11 (2021) 2309.
  19. V D Costa, et al., Physical Review Letters 85 (2000) 876.
  20. R V Hariwal,et al., Applied Surface Science Advances 100 (2022) 189.
  21. FRoccaforte, et al., Micro 2 (2022) 23.
  22. A El Hassanin, et al,. Materials (Basel). Nov 14, 22 ( 2021) 6800.
  23. A H Ramezani, et al., International Nano Letters 7 (2017) 51.
  24. A H Ramezani, et al., Modern Physics Letters B 34, 15 (2020) 2050163.
  25. S Hoseinzadeh and A H Ramezani, Journal of the Chinese Society of Mechanical Engineers 39, 5 (2018) 501.
  26. A H Ramezani, et al.,.Journal of Nanoelectronics and Optoelectronics 14, 3 (2019) 425.
  27. A H Ramezani, et al., Applied Physics A 122 (2016) 1.
  28. A H Ramezani, et al., Optik 225 (2021) 165628.
  29. A H Ramezani, et al., Applied Physics A 126 (2020) 1.
  30. A H Ramezani, et al., Electronics 10, 23 (2021) 2941.
  31. A H Ramezani, et al., Corrosion Engineering, Science and Technology 51 , 6 (2016) 393.

Home

Guide for Authors

Submit Manuscript

Reviewers

Contact Us

تحت نظارت وف بومی